Basic Information |
||||||||||
|
Material name |
Flame retardant enhancement PET |
Card |
PET0G30X2 |
|||||||
|
additive |
/ |
Exterior |
Color |
|||||||
|
Characteristic |
|
|||||||||
|
Application field |
/ |
|||||||||
|
Product property data |
||||||||||
|
Test items |
Test Methods |
unit |
Test Data |
|||||||
|
Mechanical performance |
Tensile strength |
GB/T 1040-2006 |
MPa |
126 |
||||||
|
Elongation at Break |
% |
2.9 |
||||||||
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
161 |
|||||||
|
Flexural Modulus |
MPa |
6094 |
||||||||
|
Izod impact strengt (V-notched) |
GB/T 1843-2008 |
kJ/m2 |
10.6 |
|||||||
|
Thermal performance |
Heat Deflection Temp（Tff1.8） |
GB/T 1634.2-2008 |
℃ |
202 |
||||||
|
other |
Density |
GB/T 1033-2008 |
g/cm3 |
1.60 |
||||||
|
Melt Mass Flow Rate（270℃、2.16kg） |
GB/T 3682-2000 |
g/10min |
22 |
|||||||
|
Glow wire temperature |
GB/T 5169.10-2017 |
℃ |
850(Can't afford burning) |
|||||||
|
Glow wire temperature |
℃ |
960 |
||||||||
|
Flame retardant grade |
UL 94 |
/ |
V-0 |
|||||||
|
Ash content |
GB/T 9345-2008 |
% |
29.0 |
|||||||
|
Mold shrinkage |
Machine |
GB/T 17037-2003 |
% |
0.2~0.4 |
||||||
|
Transverse |
% |
0.3~0.5 |
||||||||
|
Injection |
||||||||||
|
Dry temperature |
（130~150）℃ |
Dry time |
（4~6）h |
|||||||
|
Injection temperature |
（250~275）℃ |
Mold temperature |
/℃ |
|||||||
返回